EVA Film for Glass Lamination

price : $
  • time : 2021.09.23

Set:




  • product introduction
  • Guestbook

Specifications

1)EVA film low shrinkage

2)Useful life>15years

3)High light transmittance >92.1%

4)VE EN take partly of PVB film


0.38mm,0.4mm and 0.76mm EVA Laminated film for Glass     


1)EVA film low shrinkage

2)Useful life>15years

3)High light transmittance >92.1%

4)VE EN take partly of PVB film


Introduction


EVA Film for Laminated Glass


The latest VE/EN interlayer film is specially R&D by our own formula, which is most advanced at home and abroad.  VE film with excellent transparence, adhesion, weather resistance, and tensile strength, The useful life can up to 15years with no de-lamination and cracks.  It has passed the China National Safety Lamianted Glass Standard(GB9962-1999) and insuranced by PICC.  VE film can successfully take partly of PVB to applied in outdoor by the advantage of outstanding properties. 


Application 


Outdoor architecturall; Curtain Wall; Automobile glasses; Bullet-proof glasses; skylight; doors and windows and other outdoor decorations etc. 


Porperties


Useful life>15years


Based on the particular core technology, VE film has excellent weather-resistance, can absorb 99% UV ray radiation , can be applied in outdoor long-time with no de-lamination and cracks. 


 High light transmittance >92.1%


 Adopt DuPon EVA resin materials and differentiation technique, make the film reach different transparence at different temperature, which can meet customer's specific demands.  

Following processing data for reference.

Initial temperature

60c15mins

remark

Processing temperature

120C-125C

125C-135C

135C-150C

holding time

70"-60"

60"-45"

45"-30"

light transmittance rate

90.1%-90.6%

90.6%-91.5%

91.5%-92.1%

PRODUCT TECHNICAL PARAMETERS 


Test Item

Method

smart-PD

architectural

architectural

indoor high transparent

ordinary transparent

-EN

EN-B

Tensile strength

E&N LAB METHO

6.4MPA

8.1MPA

6.4MPA



Adhesion with glass

E&N LAB METHO

95.7N/cm    (180 peeling)

99.7N/cm       (180? peeling)

94.6N/cm(180 peeling)



Adhesion with organic polymer film

E&N LAB METHO

17.8N/cm        (180? peeling)

21.3N/cm        (180? peeling)

15.4N/cm(180? peeling)



High transmittance

E&N LAB METHO

=91.0%

=90.5%

=90.9%

=90.1%

=82.3%

Haze

E&N LAB METHO

0.29%

0.47%

0.50%

0.69%

3.23%

UV block rate

E&N LAB METHO

100%

99%

99%

65%

40%

Elongation

ASTMD638

880%

800%

880%



Shrinkage

E&N LAB METHO

=5%

=5%

=5%



Water absorptioin

E&N LAB METHO

=0.01%

=0.01%

=0.01%



Heat resistance

GB-15763.3

No bubbles and degumming





100?water for 2hrs

-2009

No bubbles and degumming

No bubbles and degumming

Humidity resistance

E&N LAB METHO

No bubbles and haze





(60?,95%RH





400hrs

No bubbles and haze

No bubbles and haze

No bubbles and haze

No bubbles and haze

Anti-aging(radiation for 3000hrs)

E&N LAB METHO

light change<3%,no yellow change

light change<3%,no yellow change

light change<3%,no yellow change



Cold and Heat shock(Cold-40?30mins,Heat80?30mins; 50circles)

E&N LAB METHO

No bubbles and degumming

No bubbles and degumming

No bubbles and degumming



Impact resistance against shot bag

GB-15763.3-2009

Qualified

Qualified

Qualified



Ball impact peeling resistance

GB-15763.3-

Qualified

Qualified

Qualified



2009

useful life

E&N LAB METHO

=20years

=15years

=15years




 

EVA4.jpgEVA5.jpgEVA23.jpg














  
 


Online Service

  For more information, please email us

 sales@benetechmachinery.com



Sent a Message to us

Click it to chat